Bohler |
C |
Si |
Mn |
Cr |
Ni |
Mo |
V |
Others |
EN / DIN |
AISI |
JIS |
Typical HRC |
W300 |
0.38 |
1.10 |
0.40 |
5.00 |
|
1.30 |
0.40 |
|
1.2343 |
H11 |
SKD6 |
42 - 50 |
|
|
|
|
|
|
|
|
|
X38CrMoV5-1 |
|
|
|
W302 |
0.39 |
1.10 |
0.40 |
5.20 |
|
1.40 |
0.95 |
|
1.2344 |
H13 |
SKD61 |
44 - 52 |
|
|
|
|
|
|
|
|
|
X40CrMoV5-1 |
|
|
|
W303 |
0.38 |
0.40 |
0.40 |
5.00 |
|
2.80 |
0.55 |
|
1.2367 |
|
|
44 - 52 |
|
|
|
|
|
|
|
|
|
X38CrMoV5-3 |
|
|
|
W350 |
0.38 |
0.20 |
0.55 |
5.00 |
|
1.75 |
0.55 |
|
patent |
|
|
44 - 52 |
ISOBLOC |
|
|
|
|
|
|
|
|
|
|
|
|
W360 |
0.50 |
0.20 |
0.25 |
4.50 |
|
3.00 |
0.55 |
|
patent |
|
|
54 - 58 |
ISOBLOC |
|
|
|
|
|
|
|
|
|
|
|
|
W400 |
0.38 |
0.20 |
0.30 |
5.00 |
|
1.30 |
0.50 |
|
~1.2343 |
~H11 |
~SKD6 |
46 - 52 |
VMR |
|
|
|
|
|
|
|
|
~X37CrMoV5-1 |
|
|
|
W403 |
0.38 |
0.20 |
0.25 |
5.00 |
|
2.80 |
0.65 |
|
~1.2367 |
|
|
46 - 52 |
VMR |
|
|
|
|
|
|
|
|
~X38CrMoV5-3 |
|
|
|
W750 |
0.02 |
0.20 |
1.40 |
15.00 |
25.00 |
1.25 |
0.30 |
Ti 2.50, Al, B |
~1.2779 |
~660 |
|
32 - 40 |
VMR |
|
|
|
|
|
|
|
|
~X6NiCrTi26-15 |
~A286 |
|
|
|
|
|
|
|
|
|
|
|
~1.4980 |
|
|
|
|
|
|
|
|
|
|
|
|
~X5NiCrTi26-15 |
|
|
|
ISOBLOC: ESR 級熱作鋼(經電渣重熔精煉)
VMR: 真空重熔級熱作鋼 |